Parameter distribution in depth magnetic microstructure epitaksialnoy film in yttrium iron garnet
Abstract
The magneticmicrostructure parameters distribution through the thickness of the epitaxial iron garnet films surface layer is investigated by the method of Conversion electron Mössbauer spectroscopy com bined with chemical etching. It is shown that the degree of iron valence change Fe3+→Fe2+ in the cry stal structure of YIG, caused by ions Pb4+, Pb2+ and Pt4+ entry, takes place in the surface layers of the film with thickness 0,15—0,18 mkm. Installing the stoichiometric values of octa and te trahedral cation sublattice populations occurs at a depth of 0,40—0,50 mkm. It is proved that the most sensitive to changes in neighbor surroundings are octahedral coordinated iron ions. Changes in the spatial orientation of the magnetic moments of the octa and tetrasublattices though the thickness of the yttrium iron garnet film surface layer are traced.
Downloads
References
Ломако И. Д., Дутов А. Г. Влияние нарушений стехиометрии и технологических приме сей на структурные свойства и поглощение в ИК диапазоне кристаллов Y3Fe5O12 // Кристаллография. — 2002. — Т. 47, № 1. — С. 128—132.
Сангвал К. Травление кристаллов: теория, эксперимент, применение. — М.: Мир, 1990. — 492 с.
Остафійчук Б. К., Федорів В. Д., Коцюбинський В. О., Мокляк В. В. Месбауерівські дослідження магнітних та електричних надтонких взаємодій в епітаксійних плівках Y3Fe5O12 // Фізика і хімія твердого тіла. — 2005. — Т. 6, № 1. — С. 60—64.
Остафійчук Б. К., Ткачук В. М., Пилипів В. М. Вплив режиму епітаксії на магнітну мікро структуру перехідних шарів плівок ЗІГ // Фізика і хімія твердого тіла. — 2000. — Т. 1, № 2. — С. 319—334.