Particularities of spatial distribution of mechanisms of the high-current relativistic electron beams influence on aluminum alloys
Keywords:
positron annihilation spectroscopy, high-current electron beams, defects, aluminumAbstract
This paper presents a study of spatial distributions of modification mechanisms in the aluminum alloy 1933 after high-current relativistic electron beam irradiation. Having used optical and scanning electron microscopy, some characteristic areas were identified which correspond to the complete electron stopping path and the adjacent zone of intense thermal effect. A higher concentration of vacancies was observed at a more distant regions using the positron annihilation spectroscopy method. It was hypothesized that the effect was caused by the shock-acoustic impact.
References
Теплопровідна паста: Пат. 102258 Україна, МПК С09K 5/00. / Б.І. Турко, Ю.Ю. Бучко, М.Р. Панасюк, В.Б. Капустяник (Україна). – № u201503434; Заявлено 14.04.15; Опубл. 26.10.15, Бюл. № 20. – 4 с. іл.
Fridlyander I. N. / Aluminum Alloys // Кiev: Komintech. – 2005. – 365 p.
Poida V. P., Pedun D. E., Bryukhovetskii V. V., Poida A. V., Sukhov R. V., Samsonik A. L., Litvinenko V. V. / Structural changes during superplastic deformation of high-strength alloy 1933 of the Al–Mg–Zn–Cu–Zr system// Phys Met Metallogr. – 2013. Vol. – 114(9). P. – 848-858.
Бойко В. И., Скворцов В. А., Фортов В. Е., Шаманин И. В.. Взаимодействие импульсных пучков заряженных частиц с веществом. М.: ФИЗМАТЛИТ. 2003, 288 с.
Блейхер Г. А., Кривобоков В. П., Пащенко О. В. Теплофизические процессы в твердом теле при воздействии мощных импульсных пучков заряженных частиц // Известия Tомского политехнического университета. – Т. 303, вып. 2. – Радиационная физика твердого тела и радиационные технологии. – 2000. –С. 71-91.
Графутин В. И., Прокопьев Е. П. Применение позитронной аннигиляционной спектроскопии для изучения строения вещества. Успехи физических наук. – 2002. ¬– Т. 172. – С. 67-83.
Anisimov S. I., Imas Ya. A., Romanov G. S. and Khodyko Yu.V. / Action of high-power radiation on metals // Springfield. – VA: National Technical Information Service. – 1971, 272 p.
Boiko V. I., Valyaev A. N., Pogrebnyak A. D. / Metal modification by high-power pulsed particle beams // PHYS-USP. – 1999. – Vol. 42(11). – P. 1139-1166.
Kobets A. G., Horodek P. R., Lonin Yu. F., Lytvynenko V. V., Ponomarev A. G., Startsev O. A., Uvarov V. T. / Melting effect on high current electron beam on aluminum alloy 1933 // Surface Engineering and Applied Electrochemistry. – 2015. – Vol. 51, No. 5. – P. 478-482.
Козырь И. Г., Бородин Р. В., Воропаев А. В. и др. Структура и свойства инструментальной стали после обработки электронным пучком и термического отпуска // Физика и химия обработки материалов. – 1998, № 3. – С. 30-33.
Horodek P., Kobets A., Meshkov I., Pavlov V., Rudakov A., Sidorin A., Yakovenko S. / Positron annihilation spectroscopy at LEPTA facility// Proceedings of RUPAC. – 2012. – WEPPC044.
Ротштейн В. П. Модификация структуры и свойств металлических материалов интенсивными импульсными электронными пучками. Автореф. дисс. докт. ф.-м. н.: 01.04.07.- Томск. – 1995. – 37 с.